RESEARCH ARTICLE

Comparative Evaluation of Compressive Strength and Flexural Strength of Self-cured Cention N with Dual-cured Cention N: An In Vitro Study

Ks Fousiya, VR Balagopal, KJ Suresh, Parvathy Kumaran, Arun M Xavier, Medhini M Menon

Citation Information : Fousiya K, Balagopal V, Suresh K, Kumaran P, Xavier AM, Menon MM. Comparative Evaluation of Compressive Strength and Flexural Strength of Self-cured Cention N with Dual-cured Cention N: An In Vitro Study. Int J Clin Pediatr Dent 2022; 15 (2):210-214.

DOI: 10.5005/jp-journals-10005-2363

License: CC BY-NC 4.0

Published Online: 01-04-2022

Copyright Statement:  Copyright © 2022; The Author(s).


Abstract

Aim and objective: This study aimed to investigate and compare compressive strength and flexural strength of self-cured Cention N with dual-cured Cention N. Materials and methods: Cention N is mixed according to the proportions, as mentioned by the manufacturer. Dual cured samples are cured using a diode that emits blue light. Cylindrical plexiglass split mold of dimension 6 mm height, and 4 mm diameter used to fabricate samples for compressive strength. Compressive strength tested using Instron universal testing machine. Rectangular plexiglass split mold of dimension 25 mm length, 2 mm height, and 2 mm width were used to fabricate samples for flexural strength. Flexural strength tested using Instron universal testing machine. To compare the mean values independent t-test was used and the significance of the study was measured by calculating a p-value. Result: There is no statistically significant difference between compressive strength and flexural strength of self-cured Cention N with dual-cured Cention N. Conclusion: The type of polymerization does not affect flexural strength and compressive strength of Cention N. Clinical significance: Self-curing polymerization alone is sufficient for Cention N to achieve adequate compressive strength and flexural strength. So it can be inserted as a single layer on a prepared cavity and to fasten curing additional light curing can be used.


HTML PDF Share
  1. Mann JS, Sharma S, Maurya S et al. Cention N: A review. Int J Curr Res 2018;10(5):69111–69112.
  2. Bayne SC, Ferracane JL, Marshall GW, et al. The evolution of dental materials over the past century: silver and gold to tooth color and beyond. J Dent Res 2019;98(3):257–265. DOI: 10.1177/0022034518822808
  3. Moszner N. State of the art: Photopolymerization in dentistry. IvoclarVivadent Report. Liechtenstein: IvoclarVivadent AG. 2013;19.
  4. Vandewalker JP, Casey JA, Lincoln TA, et al. Properties of dual-cure, bulk-fill composite resin restorative materials. Gen Dent 2016;64(2):68–73. PMID: 26943093.
  5. Anusavice KJ, Shen C, Rawls HR, editors. Phillips’ science of dental materials. Elsevier Health Sciences; 2012.
  6. Todd JC. Scientific Documentation: Cention N. Ivoclar–Vivadent Press: Schaan, Liechtenstein. 2016:1–58.
  7. Ilie N. Comparative effect of self-or dual-curing on polymerization kinetics and mechanical properties in a novel, dental-resin-based composite with alkaline filler. Running resin-composites with alkaline fillers. Materials (Basel) 2018;11(1):108. DOI: 10.3390/ma11010108
  8. AlQahtani MQ, AlShaafi MM, Price RB. Effects of single-peak vs poly wave light-emitting diode curing lights on the polymerization of resin cement. J Adhes Dent 2013;15(6):547–551. DOI: 10.3290/j.jad.a29634
  9. AlShaafi MM. Factors affecting polymerization of resin-based composites: a literature review. Saudi Dent J 2017;29(2):48–58. DOI: 10.1016/j.sdentj.2017.01.002
  10. Ozturk B, Cobanoglu N, Cetin AR, et al. Conversion degrees of resin composites using different light sources. Eur J Dent 2013;7(1):102–109. PMID: 23407765; PMCID: PMC3571517.
  11. Peutzfeldt A. Dual-cure resin cement: in vitro wear and effect of quantity of remaining double bonds, filler volume, and light curing. Acta Odontol Scand 1995;53(1):29–34. DOI: 10.3109/00016359509005941
  12. Rueggeberg FA. From vulcanite to vinyl, a history of resins in restorative dentistry. J Prosthet Dent 2002;87(4):364–379. DOI: 10.1067/mpr.2002.123400
  13. Moszner N, Fischer UK, Ganster B, et al. Benzoyl germanium derivatives as novel visible light photoinitiators for dental materials. Dent Mater 2008;24(7):901–907. DOI: 10.1016/j.dental.2007.11.004
  14. Ilie N, Simon A. Effect of curing mode on the micro-mechanical properties of dual-cured self-adhesive resin cements. Clin Oral Investig 2012;16(2):505–512. DOI: 10.1007/s00784-011-0527-x
  15. Fonseca RG, Cruz CA, Adabo GL. The influence of chemical activation on the hardness of dual-curing resin cements. Braz Oral Res 2004;18(3):228–232. DOI: 10.1590/s1806- 83242004000300009
  16. Tanimoto Y, Hayakawa T, Nemoto K. Analysis of photopolymerization behaviour of UDMA/TEGDMA resin mixture and its composite by differential scanning calorimetry. J Biomed Mater Res B Appl Biomater 2005;72(2):310–315. DOI: 10.1002/jbm.b.30151
  17. Moszner N, Fischer UK, Angermann J, et al. A partially aromatic urethane dimethacrylate as a new substitute for Bis-GMA in restorative composites. Dent Mater 2008;24(5):694–699. DOI: 10.1016/j.dental.2007.07.001
  18. Sideridou I, Tserki V, Papanastasiou G. Effect of chemical structure on degree of conversion in light-cured dimethacrylate-based dental resins. Biomaterials 2002;23(8):1819–1829. DOI: 10.1016/s0142-9612(01)00308-8
  19. Dickens SH, Stansbury JW, Choi KM, et al. Photopolymerization kinetics of methacrylate dental resins. Macromolecules 2003;36(16): 6043–6053. DOI: 10.1021/ma021675k
  20. Monteiro GQ, Montes MA. Evaluation of linear polymerization shrinkage, flexural strength and modulus of elasticity of dental composites. Mater Res 2010;13(1):51–55. DOI: 10.1590/s1516-14392010000100012
  21. Chole D. In Vitro Comparision of Flexural Strength of Cention-N, Bulk-Fill Composites, Light-Cure Nanocomposites And Resin-Modified Glass Ionomer Cement. IOSR-JDMS 2018;17(10):79–82. DOI: 10.9790/0853-1710087982.
PDF Share
PDF Share

© Jaypee Brothers Medical Publishers (P) LTD.